Slurry for chemical-mechanical polishing of metals and use thereof

ABSTRACT

A composition and a method for chemical mechanical polishing. The composition includes a surfactant anion an alkyl alcohol and a diluent. The composition further includes abrasive particles and an oxidizer. The method includes providing the composition on a surface to be polished and polishing the surface by contacting the surface with a polishing pad.

FIELD OF THE INVENTION

The present invention relates to slurry compositions that are useful forpolishing or planarizing a surface. The present invention is especiallyuseful for polishing or planarizing copper used as interconnect wiringin integrated circuit devices such as semiconductor wafers containingcopper damascene and dual damascene wires. The present invention alsorelates to polishing processes employing the compositions of the presentinvention.

BACKGROUND

When chemical-mechanical polishing is used to form damascene anddual-damascene wires during the fabrication of integrated circuits theuniformity of the polishing process is most important in reducingdefects and increasing yields. The industry is always welcoming toimproved polishing methods. The embodiments of the present inventionprovide a significant increase in uniformity of the chemical-mechanicalpolishing process.

SUMMARY

A first aspect of the present invention is a composition, comprising: aminimum of about 32% by weight of a surfactant anion; between about 0.8%by weight and about 1.2% by weight of an alkyl alcohol; and a diluent.

A second aspect of the present invention is a composition, consistingessentially of: a minimum of about 32% by weight of a surfactant anion;between about 0.8% by weight and about 1.2% by weight of an alkylalcohol; and a diluent.

A third aspect of the present invention is a slurry composition,comprising: between about 0.5% by weight and about 6% by weight abrasiveparticles; between about 1 gm/liter and about 50 gm/liter of anoxidizer; between about 0.1 ml/liter and about 100 ml/liter ofsurfactant anion; between about 0.003 ml/liter and about 3.05 ml/literof an alkyl alcohol; and a diluent.

A fourth aspect of the present invention is a slurry composition,consisting essentially of: between about 0.5% by weight and about 6% byweight abrasive particles; between about 1 gm/liter and about 50gm/liter of an oxidizer; between about 0.1 ml/liter and about 100ml/liter of surfactant anion; between about 0.1 gm/liter and about 5gm/liter of a copper corrosion inhibitor; between about 0.003 ml/literand about 3.05 ml/liter of an alkyl alcohol; and a diluent.

A fifth aspect of the present invention is a method, comprising:providing a slurry composition according to the third aspect on asurface to be polished; and polishing the surface by contacting thesurface with a polishing pad.

A sixth aspect of the present invention is a method, comprising:providing a slurry composition according to the fourth aspect on asurface to be polished; and polishing the surface by contacting saidsurface with a polishing pad.

These and other aspects of the invention are described below.

BRIEF DESCRIPTION OF THE DRAWINGS

The features of the invention are set forth in the appended claims. Theinvention itself, however, will be best understood by reference to thefollowing detailed description of illustrative embodiments when read inconjunction with the accompanying drawings, wherein:

FIGS. 1A through 1H are cross-sectional views illustrating an exemplarymethod of fabricating a damascene wire of an integrated circuitaccording to embodiments of the present invention;

FIG. 2 is a cross-sectional view illustrating the electricallyconductive layers used to fabricate exemplary damascene and dualdamascene wires according to embodiments of the present invention;

FIG. 3 is a cross-section view illustrating an exemplary dual-damascenewire contacting a damascene wire according to embodiments of the presentinvention;

FIG. 4 is a cross-section view illustrating a dishing defect in anexemplary damascene wire;

FIG. 5 is a plot of surface tension versus surfactant concentration fortwo concentrations of the additive octanol according to embodiments ofthe present invention;

FIG. 6 is a chart relating surface tension, octanol concentration anddishing according to embodiments of the present invention;

FIG. 7 is a schematic diagram of an exemplary slurry mixing and deliverysystem that may be used to practice the embodiments of the presentinvention; and

FIG. 8 is a schematic diagram of an exemplary chemical-mechanical polishtool that may be used to practice the embodiments of the presentinvention.

DETAILED DESCRIPTION

A surfactant composition according to embodiments of the presentinvention includes an alkyl alcohol and a surfactant. This surfactantcomposition is added to a chemical-mechanical-polish (CMP) slurry usedfor polishing damascene and dual-damascene wires during fabrication ofintegrated circuits. The inclusion of an alkyl alcohol in the CMP slurrycomposition acts to increase the uniformity of the polishing processwithout increasing the amount of corrosion of the wires by reducing thesurface tension of the slurry.

A damascene process is one in which wire trenches are formed in adielectric layer and an electrical conductor of sufficient thickness tofill the trenches is deposited in the trenches and on a top surface ofthe dielectric. A CMP process is performed to remove excess conductorand make the surface of the conductor co-planar with the surface of thedielectric layer to form damascene wires. There are two types ofdual-damascene processes. A via first dual-damascene process is one inwhich via openings are formed through the entire thickness of adielectric layer followed by formation of trenches part of the waythrough the dielectric layer in any given cross-sectional view. A trenchfirst dual-damascene process is one in which trenches are formed partway through the thickness of a dielectric layer followed by formation ofvias inside the trenches the rest of the way through the dielectriclayer in any given cross-sectional view. An electrical conductor ofsufficient thickness to fill the trenches and via opening is depositedon a top surface of the dielectric and a CMP process is performed tomake the surface of the conductor in the trench co-planar with thesurface the dielectric layer to form dual-damascene wires havingintegral vias.

Surfactant compositions of embodiments of the present invention includea mixture of a surface active agent (i.e., surfactant) and an alkylalcohol in water or other suitable solvent such as methanol, ethanol,ethylene glycol and glycerol. Examples of suitable surfactants includeNa-alkyl sulfates, Na-alkyl sulfonates, quarternary such as tetramethylammonium halides, cetyl trimethy ammonium halides, hydroxides, nonylethers and combinations thereof. Preferred surface active agents aresulfates such as Na-hexyl, -heptyl, -octyl, -nonyl and -lauryl sulfateswith Na-octyl sulfate being most preferred. Examples of suitable alkylalcohols include but are not limited to alkyl mono-alcohols having 6 to14 carbon atoms, straight chain alkyl mono-alcohols having 6 to 14carbon atoms, straight chain alkyl primary mono-alcohols having 6 to 14carbon atoms, branched-chain alkyl mono-alcohols, alkyl poly-alcoholshaving 6 to 14 carbon atoms, straight chain alkyl poly-alcohols having 6to 14 carbon atoms, straight chain alkyl primary poly-alcohols having 6to 14 carbon atoms, and branched-chain alkyl poly-alcohols. A primaryalcohol is an alcohol where the OH group is connected to a primarycarbon atom. A primary alcohol contains a —CH₂OH group. Preferred alkylalcohols have the formula C_(n)(H₂)_(n+1)OH where n has a value of 6 to14. Preferred alkyl alcohols have the formula CH₃(CH₂)_(m)OH where m hasa value between 5 and 13. A preferred alkyl alcohol is 1-octanol.

In one example, surfactant compositions of embodiments of the presentinvention include between about 0.1% by weight and about 1.5% by weightof alkyl alcohol or a mixture of two or more alkyl alcohols. In oneexample, surfactant mixtures of embodiments of the present inventioninclude between about 0.1% by weight and about 1.5% by weight ofoctanol. In one example, surfactant mixtures of embodiments of thepresent invention includes between about 30% by weight and about 35% byweight of surfactant. In one example, surfactant mixtures of embodimentsof the present invention includes between about 30% by weight and about35% by weight of sodium octyl sulfate.

An exemplary surfactant composition comprises (i) between about 0.8% byweight and about 1.2% by weight alkyl alcohol (e.g., octanol), (ii) aminimum of about 32% by weight of surfactant anions (e.g., octyl sulfateanion of (e.g., sodium octyl sulfate)), and (iii) a diluent (e.g.,water). The viscosity of this surfactant composition is no greater thanabout 150 centipoise at 25° C. A 10% by weight solution of thissurfactant composition in water has a pH of between about 7 and about 9.Additionally, the surfactant composition may include a maximum of about1.0% by weight of a sulfate ion source (e.g., sodium sulfate), and/or amaximum of about 0.1% by weight of a chloride ion source (e.g., sodiumchloride).

An exemplary surfactant composition consists essentially of (i) betweenabout 0.8% by weight and about 1.2% by weight alkyl alcohol (e.g.,octanol), (ii) a minimum of about 32% by weight of anionic surfactant(e.g., octyl sulfate anion of (e.g., sodium octyl sulfate)), and (iii) adiluent (e.g., water). The viscosity of this surfactant composition isno greater than about 150 centipoise at 25° C. A 10% by weight solutionof this surfactant composition in water has a pH of between about 7 andabout 9. In one example, in excess of 0.5% by weight of NaCl (0.3% byweight chloride ion) in the surfactant composition was found to morethan offset the reduction in dishing due to the presence of the alkylalcohol. In one example, in excess about 1% by weight of organic amineor ammonium ion (NH₄+) was found to more than offset the reduction indishing due to the presence of the alkyl alcohol.

CMP slurry compositions according to embodiments of the presentinvention include the aforementioned surfactant/alkyl alcoholcomposition as a component of the CMP slurry. Alternatively, instead ofincluding a premixed surfactant/alkyl alcohol mixture, CMP slurrycompositions according to embodiments of the present invention mayinclude the aforementioned surfactants and alkyl alcohols as separatecomponents. Either way, in one example, CMP slurry compositionsaccording to embodiments of the present invention include between about0.1 ml/liter and about 100 ml/liter of surfactant and between about0.003 ml/liter and about 3.05 ml/liter of alkyl alcohol.

CMP slurry compositions according to embodiments of the presentinvention include an oxidizing agent. Suitable oxidizing agents includeoxidizing metal salts, oxidizing metal complexes, oxidizing acids suchas nitric, persulfuric, peracetic and periodic acids, iron salts such asnitrates and sulfates; potassium ferricyanide, hydrogen peroxide,aluminum salts, sodium salts, potassium such as potassium iodate,ammonium salts such as ammonium cerium nitrate, phosphonium salts,chlorates, perchlorates such as potassium percholate, nitrates,permaganates such as potassium permanganate, persulfates and mixturesthereof. Preferred oxidizing agents are ferric nitrate and hydrogenperoxide, either together or singly.

In one example, CMP slurry compositions of embodiments of the presentinvention include between about 1 gm/liter and about 50 gm/literoxidizer with between about 10 gm/liter and about 40 gm/liter preferred.

CMP slurry compositions according to embodiments of the presentinvention, when employed to polish copper, also include a coppercorrosion inhibitor. When the compositions are used for polishing Al orW, they can and preferably also include a copper corrosion inhibitor.Typical copper corrosion inhibitors include imidozoles, triazoles suchas 1,2,4-triazole and benzotriazole. In one example, CMP slurrycompositions of embodiments of the present invention include betweenabout 0.1 gm/liter and about 5 gm/liter copper corrosion inhibiter withabout 2.5 gm/liter preferred.

CMP slurry compositions according to embodiments of the presentinvention also include abrasive particles. Examples of suitable abrasiveparticles include alumina, silica, ferric oxide, zirconia, ceria, andtitanium dioxide and mixtures thereof with alumina preferred. Also, theabrasive particles can include a dual-valent rare earth ion orsuspension of its colloidal hydroxide, wherein the rare earth ion is inits higher valent form. Examples of some suitable rare earths are Ce⁴⁺,Pr⁴⁺ and Tb⁴⁺ or suspensions of their colloidal oxides, such as ceriumoxide. The dual-valent rare earth or rare earth oxide colloid acts as anoxidation catalyst.

In one example, abrasive particles have a particle size of between about10 nm to about 1000 nm and preferably between about 50 nm and about 200nm. In one example, CMP slurry compositions of embodiments of thepresent invention include between about 0.5% by weight and about 6% byweight abrasive particles with between about 2% by weight and about 4%by weight preferred.

Mixtures of abrasives can be employed when desired. An exemplaryabrasive mixture includes alumina (between about 0.1% by weight andabout 6% by weight), silica (between about 0.1% by weight and about 5%by weight) and zirconia (between about 0.1 to about 6% by weight).Another exemplary abrasive mixture includes alumina (between about 1% byweight and about 5% by weight) and silica (between about 1% by weightand about 20% by weight).

Slurry compositions according to embodiments of the present inventionare preferably aqueous slurries. Other types of suitable slurriesinclude those using the organic solvents such as propylene carbonate andmono and polyhydric alcohols such as methanol, ethanol, ethylene glycoland glycerol as diluents. Mixtures of the aforementioned diluents aswell as mixtures of the aforementioned diluents with water can be used.

CMP slurry compositions according to embodiments of the presentinvention also include both a chloride ion source and a sulfate ionsource. The chloride ion and sulfate ion sources are typically presentas salts including salts of alkali metals such as sodium and potassium;alkaline earth metals such as calcium; and ammonia. A preferred chlorideion source is sodium chloride, and preferred sulfate ion source issodium sulfate.

In one example, the amount of chloride ion source is between about 0.001gm/liter and about 5 gm/liter with between about 0.05 gm/liter and about0.1 gm/liter preferred. In one example, the amount of sulfite ion sourceis between about 0.001 gm/liter and about 20 gm/liter with between about1 gm/liter and about 3 gm/liter preferred. All or part of the allowableamount of chloride ion source may be supplied by the surfactantcomposition. All or part of the allowable amount of sulfate ion sourcemay be supplied by the surfactant composition.

The CMP slurry compositions of embodiments of the present invention areuseful for polishing copper (Cu), tungsten (W), and aluminum (Al),alloys of copper, alloys of aluminum and alloys of tungsten and isselective to Cu, W and Al with respect to titanium (Ti), titaniumnitride (TiN), tantalum (Ta) and tantalum nitride (TaN). Thesurfactant/alkyl alcohol compositions of the present invention andespecially the preferred concentrations of the components result inreduced dishing of Cu wires at low without excessive corrosion. (seeFIG. 4).

An exemplary CMP slurry for forming damascene and dual-damascene copperwires during the fabrication of integrated circuits comprises (i)between about 0.5% by weight and about 6% by weight abrasive (e.g.,alumina) with between about 2% by weight and about 4% by weightpreferred, (ii) between about 1 gm/liter and about 50 gm/liter of anoxidizer (e.g., ferric nitrate) with between about 10 gm/liter and about40 gm/liter preferred, (iii) between about 0.1 ml/liter and about 100ml/liter of surfactant anion (e.g., octyl sulfate anion of (e.g., sodiumoctyl sulfate)) (iv) between about 0.1 gm/liter and about 5 gm/liter acopper corrosion inhibitor (e.g., benzothiazole) with about 2.5 gm/literpreferred), (v) between about 0.003 ml/liter and about 3.05 ml/liter ofan alkyl alcohol (e.g., octanol), and (vi) a diluent (e.g., water).Additionally, the slurry composition may include between about 0.001gm/liter and about 5 gm/liter of a chloride ion source (e.g., sodiumchloride) with between about 0.05 gm/liter and about 0.1 gm/literpreferred and/or between about 0.001 gm/liter and about 20 gm/liter asulfate ion source (e.g., sodium sulfate) with between about 1 gm/literand about 3 gm/liter preferred.

An exemplary CMP slurry for forming damascene and dual-damascene copperwires during the fabrication of integrated circuits consists essentiallyof (i) between about 0.5% by weight and about 6% by weight abrasive(e.g., alumina) with between about 2% by weight and about 4% by weightpreferred, (ii) between about 1 gm/liter and about 50 gm/liter of anoxidizer (e.g., ferric nitrate) with between about 10 gm/liter and about40 gm/liter preferred, (iii) between about 0.1 ml/liter and about 100ml/liter of surfactant anion (e.g., octyl sulfate anion of (e.g., sodiumoctyl sulfate)), (iv) between about 0.1 gm/liter and about 5 gm/liter acopper corrosion inhibitor (e.g., benzotriazole) with about 2.5 gm/literpreferred), (v) between about 0.003 ml/liter and about 3.05 ml/liter ofan alkyl alcohol (e.g., octanol), and (vi) a diluent (e.g., water). Itis advantageous that there is less than 1% by weight of sodium citrate,NaNO₃, Na₂HPO₄, sodium oxalate, Na₂SiF₆ and NaF n the slurrycomposition. In one example, in excess of 0.5% by weight of NaCl (0.3%by weight chloride ion) in the slurry composition was found to more thanoffset the reduction in dishing due to the presence of the alkylalcohol. In one example, in excess of about 1% by weight of organicamine or ammonium ion (NH₄+) in the slurry composition was found to morethan offset the reduction in dishing due to the presence of the alkylalcohol.

FIGS. 1A through 1H are cross-sectional views illustrating an exemplarymethod of fabricating a damascene wire of an integrated circuitaccording to embodiments of the present invention. In FIG. 1A, asemiconductor substrate 100 includes a field effect transistor (FET) 105including source drains 110A and 110B separated by a channel region 115(of substrate 100) under a gate 120. Gate 120 is electrically isolatedfrom source/drains 110A and 110B and channel region 115 by a gatedielectric 125. A perimeter of FET 105 is surrounded by trench isolation130. Trench isolation is formed in substrate 100. Formed on substrate100 is a dielectric copper diffusion barrier layer 135. Formed onbarrier layer 135 is a dielectric layer 140. Formed on a top surface ofdielectric layer 140 is an interlevel dielectric (ILD) layer 145 andformed on a top surface of ILD 145 is a dielectric hardmask layer 150.Formed in dielectric layer 140 and extending from a top surface ofdielectric layer 140, through barrier layer 135 to a top surface ofsubstrate 100 is an electrically conductive stud contact 155.

In FIG. 1B, a patterned photoresist layer 160 is formed having anopening 165 therein using a photolithographic process. Aphotolithographic process is one in which a photoresist layer is appliedto a surface of a substrate, the photoresist layer exposed to actinicradiation through a patterned photomask and the exposed photoresistlayer developed to form a patterned photoresist layer. When thephotoresist layer comprises positive photoresist, the developerdissolves the regions of the photoresist exposed to the actinicradiation and does not dissolve the regions where the patternedphotomask blocked (or greatly attenuated the intensity of the radiation)from impinging on the photoresist layer. When the photoresist layercomprises negative photoresist, the developer does not dissolve theregions of the photoresist exposed to the actinic radiation and doesdissolve the regions where the patterned photomask blocked (or greatlyattenuated the intensity of the radiation) from impinging on thephotoresist layer. The photoresist layer may optionally be baked at oneor more of the following steps: prior to exposure to actinic radiation,between exposure to actinic radiation and development, afterdevelopment. A top surface of polish stop later 150 is exposed in thebottom of opening 165.

In FIG. 1C, hardmask layer 150 has been removed (i.e., by reactive ionetch (RIE)) where not protected by patterned photoresist layer 160 (seeFIG. 1B) to form a trench 175 and the patterned photoresist layerremoved. The top surface of ILD 145 is exposed in the bottom of trench175.

In FIG. 1D, trench 175 is extended through ILD 145 into dielectric layer140 (i.e., using hardmask layer 150 as a patterned hardmask for an RIEprocess). Trench 175 is recessed into dielectric layer 140 deep enoughto expose at least the top surface of stud contact 155.

In FIG. 1E, an electrically conductive liner layer 180 is formed on thetop surface of hardmask layer 150, and previously exposed surfaces ofdielectric layer 140, ILD layer 145, hardmask layer 150 and stud contact155 in trench 175. In FIG. 1F, an electrically conductive core conductorlayer 185 is formed on a top surface of liner layer 180 so trench 175 iscompletely filled.

In FIG. 1G, a first CMP process is performed to coplanarize the topsurfaces of core conductor layer 185 and liner layer 180. In FIG. 1H, asecond CMP process is performed to remove regions of liner layer 185that are on hardmask layer 150 and to remove hardmask layer 150 (seeFIG. 1G) and coplanarize the top surface of ILD 145 and a damascene wire190. Damascene wire 190 consists of a core conductor 185A having a liner180A on its bottom surface and sidewalls, where liner 180A was derivedfrom liner layer 180 and core conductor was derived from core conductorlayer 185. The first and second CMP processes utilize the slurrycompositions described supra.

FIG. 2 is a cross-sectional view illustrating the electricallyconductive layers used to fabricate exemplary damascene and dualdamascene wires according to embodiments of the present invention. InFIG. 2, liner layer 180 includes a first layer 182 and a second layer183. In one example, first layer 182 is TiN and second layer 183 is Ti.In one example, first layer 182 is TaN and second layer 183 is Ta. Coreconductor layer 185 includes an evaporated copper seed layer 187 and aplated copper layer 188. Copper seed layer 187 is formed on second layer183.

FIG. 3 is a cross-section view illustrating an exemplary dual-damascenewire contacting a damascene wire according to embodiments of the presentinvention. In FIG. 3, an additional dielectric copper diffusion barrierlayer 195 is formed on the top surfaces of damascene wire 190 and anadditional ILD layer 200 formed on barrier layer 195. ILD layer 200 mayinclude multiple dielectric layers. A dual damascene wire 205 is formedin ILD 200. Wire 205 includes an electrically conductive liner 210 and acore conductor 215. Wire 205 includes a wire portion 220 and a viaportion 225. Via portion 225 of wire 205 physically and electricallycontacts wire 190. The materials for wire 205 are the same as describedfor wire 190. The CMP processes used to form wire 205 are similar to theCMP processes used to form wire 190 including the slurry.

FIG. 4 is a cross-section view illustrating a dishing defect in anexemplary damascene wire. In FIG. 4, a damascene wire 250 is formed in adielectric layer 255. Wire 250 includes an electrically conductive liner260 and a core conductor 265. ILD layer 255 has a top surface 270. Thetop surface of the exposed edge 275 of liner 260 is coplanar with topsurface 270 of ILD layer 255. The dashed line 280 indicates the desiredtop surface of core conductor 265 after CMP. The actual top surface 285is dished or concave relative to dashed line 280. Top surface 285 isdished a maximum distance D. When the value of D exceeds a target valuefor a given wiring level, defects such a shorts between wires on thesame wiring level can occur. In one example, D is between about 0 Å andabout 2000 Å. D can not be negative.

An integrated circuit may utilize multiple wiring levels employingcopper damascene and dual damascene wire. One or more of the multiplelevels may be fabricated using fabrication steps described for wires 190and 205. One or more of the multiple levels may be fabricated using aCMP slurry according to embodiments of the present invention. One ormore of the ILD dielectric layers described supra may comprise a low-Kdielectric material. A low K dielectric material is defined as amaterial having a permittivity of 3 or less.

FIG. 5 is a plot of surface tension versus surfactant concentration fortwo concentrations of the additive octanol according to embodiments ofthe present invention. The surfactant was sodium octyl sulfate. Curve290A is a plot of surface tension vs. concentration of surfactant with0.157% by weight of octanol added to an aqueous solution of thesurfactant and concentration of surfactant between 0 and 1.0% by weighsurfactant. Curve 290B is a plot surface tension vs. concentration ofsurfactant with 1.003% by weight of octanol added to an aqueous solutionof the surfactant and concentration of surfactant between 0 and 1.0% byweigh surfactant. In curve 290A the ratio of sodium octyl sulfate tooctanol was about 210:1. In curve 290B the ratio of sodium octyl sulfateto octanol was about 33:1. Curves 290A and 290B show that the additionof octanol can increase the ability of surfactant to lower the surfacetension of water. Lowering the surface tension increases the wetabilityof the surface being CMPed and increases the uniformity as shown in FIG.6. While it appears that the same surface tension can be obtained withhigher amounts of surfactant and less octanol, however the higher thesurfactant concentration the more copper corrosion is seen. Thus it ispreferred to use less surfactant and more octanol to achieve a givensurface tension.

FIG. 6 is a chart relating surface tension, octanol concentration anddishing according to embodiments of the present invention. In FIG. 6,four CMP slurries were prepared using 0.35% by weight surfactant (sodiumoctyl sulfate). The first contained no octanol. The second contained0.35% by weight of octanol. The third contained 0.70% by weight ofoctanol. The fourth contained 1.4% by weight of octanol. Both productwafers (bars labeled P) and test wafers (bars labeled T) were CMPed. Theaddition of 1-oxtanol significantly reduced the amount of dishing fromabout 1350 Å without octanol to about 1000 Å on the product wafers andfrom about 900 Å without octanol to about 625 Å on the test wafers.Curve 295 is a plot of the surface tension vs. octanol concentration.Without octanol, the surface tension was about 34 dynes/cm². Withoctanol, the surface tension ranged from about 30 dynes/cm² to about 27dynes/cm² showing the reduction in dishing and in surface tensioncorrelated. Thus no undue experimentation is required as simple surfacetension measurements can point to a range of surfactant/alkyl alcoholconcentrations to use in dishing experiments which require test orproduct wafers and a CMP apparatus along with its slurry mix anddelivery system. Dishing was measured using a P10 profilometer.

FIG. 7 is a schematic diagram of an exemplary slurry mixing and deliverysystem that may be used to practice the embodiments of the presentinvention. In FIG. 7, a slurry mixing and delivery system 300 includes aslurry mixing tank, a slurry holding tank, CMP tools 315 and 320 and asurfactant tank 325. Surfactant tank 325 holds a solution of surfactantto which an alkyl alcohol as described supra has been added. Thesurfactant/alkyl alcohol is pumped by a pump 330 through a filter 335 toslurry mixing tank 305. Also added to slurry mixing tank are a diluent(e.g., water), an oxidizer (e.g., ferric nitrate), additives (e.g.,chloride and sulfate anion sources and copper corrosion inhibiter) andan abrasive (e.g., alumina). Alternatively, the alkyl alcohol can beadded to slurry mixing tank 305 directly. The mixed slurry istransferred to slurry holding tank 310 by pump 340. From slurry holdingtanks 310, pumps 345 and 350 deliver slurry to CMP tools 315 and 320respectively. Used slurry from CMP tools 315 and 320 is filtered byfilters 355 and 360 respectively and delivered back to slurry holdingtank 310. Provision is made by valves 365 and 370 to dispose used slurryto a waste stream for collection or treatment. While two CMP tools areillustrated, there may be one or more CMP tools.

FIG. 8 is a schematic diagram of an exemplary chemical-mechanical polishtool that may be used to practice the embodiments of the presentinvention. In FIG. 8, a CMP apparatus 400 for planarization of asemiconductor substrate 405 placed top surface down on a pad 420 on arotatable table 410. Pad 420 normally comprises a porous material. Thepad material is capable of absorbing particulate matter such as silicaor other abrasive materials.

Substrate 405 is held in a carrier 425. The backside of substrate 405 isheld in contact with an insert pad 430 in carrier 425 by a vacuum. Aretaining ring 435 is employed to prevent wafer 405 from slippinglaterally from beneath carrier 425. A downward pressure “F” is appliedby means of a shaft 440 attached to the backside of carrier 425. In oneexample, using the slurry compositions according to embodiments of thepresent invention, F is between about 2 psi and about 6 psi. Thispressure is used to facilitate CMP of the upper surface of substrate405.

During operation, carrier 425 typically rotates in a circular motionrelative to table 410. Rotational movement of carrier 425 may beprovided by coupling a motor (not shown) to shaft 440. Table 410 alsorotates by means of a shaft 445. Rotational movement of table 410 may beprovided by coupling a motor (not shown) to shaft 445. In one example,the relative rotational movements of carrier 425 and table 410 arecounter-directional and, carrier 425 remains in a stationary positionrelative to shaft 445. In one example, carrier 425 rotates between about10 and about 70 RMP with between about 15 RPM and 60 RPM preferred. Inone example, table 410 rotates between about 10 and about 90 RMP withbetween about 40 RPM and 80 RPM preferred

CMP apparatus 400 further includes an optional temperature controller450 for heating a heat transfer fluid and pumping the heat transferfluid through a pipe 455. Pipe 455 passes through the interior of table410 so that the temperature of table 410 may be increased above roomtemperature during the polishing process. Heating of table 410 isoptional.

CMP apparatus 400 further includes a pipe 460 for delivering slurry ontothe surface of pad 420 during polishing. After being pumped thoroughpipe 460, the slurry is directed onto the surface of pad 420 by nozzle465. In an optional embodiment, the slurry is heated by temperaturecontroller 450 through a heat exchanger 470. Heat exchanger 470thermally couples portions of pipes 455 and 460 together so that theslurry passing through pipe 460 is maintained at the same temperature asthat of the heating fluid flowing through pipe 455.

This the embodiments of the present invention provide a surfactantmixture, a slurry using the surfactant mixture and a method using theslurry that result in increased chemical polishing uniformity ofdamascene and dual damascene copper wires in integrated circuits.

The description of the embodiments of the present invention is givenabove for the understanding of the present invention. It will beunderstood that the invention is not limited to the particularembodiments described herein, but is capable of various modifications,rearrangements and substitutions as will now become apparent to thoseskilled in the art without departing from the scope of the invention.Therefore, it is intended that the following claims cover all suchmodifications and changes as fall within the true spirit and scope ofthe invention.

What is claimed is:
 1. A method, comprising: providing an aqueous slurrycomposition on a surface to be polished, said slurry compositioncomprising: between about 0.5% by weight and about 6% by weight abrasiveparticles; between about 1 gm/liter and about 50 gm/liter of ferricnitrate; between about 0.1 ml/liter and about 100 ml/liter of surfactantanion; between about 0.003 ml/liter and about 3.05 ml/liter of octanol;and water as a diluent; and polishing said surface by contacting saidsurface with a polishing pad.
 2. The method of claim 1, wherein saidsurface is selected from the group consisting of copper, aluminum,tungsten, alloys of copper, alloys of aluminum and alloys of tungsten.3. The method of claim 1, wherein during said polishing, said surface ispressed into said polishing pad with a down force while said surface andsaid polishing pad are rotating about axes perpendicular to said surfaceand a top surface of said polishing pad respectively.
 4. The method ofclaim 1, wherein said surfactant anion is derived from sodium octylsulfate.
 5. A method, comprising: providing an aqueous slurrycomposition consisting essentially of: between about 0.5% by weight andabout 6% by weight abrasive particles; between about 1 gm/liter andabout 50 gm/liter of ferric nitrate; between about 0.1 ml/liter andabout 100 ml/liter of surfactant anion; between about 0.1 gm/liter andabout 5 gm/liter of a copper corrosion inhibitor; between about 0.003ml/liter and about 3.05 ml/liter of octanol; and water as a diluent; andpolishing said surface by contacting said surface with a polishing pad.6. The method of claim 5, wherein said surface is selected from thegroup consisting of copper, aluminum, tungsten, alloys of copper, alloysof aluminum and alloys of tungsten.
 7. The method of claim 5, whereinduring said polishing, said surface is pressed into said polishing padwith a down force while said surface and said polishing pad are rotatingabout axes perpendicular to said surface and a top surface of saidpolishing pad respectively.
 8. The method of claim 5, wherein saidsurfactant anion is derived from sodium octyl sulfate.
 9. The method ofclaim 1 wherein said octanol is 1-octanol.
 10. The method of claim 1,said slurry composition further comprising: between about 0.001 gm/literand about 5 gm/liter of a chloride ion source; and between about 0.001gm/liter and about 20 gm/liter a sulfate ion source.
 11. The method ofclaim 1, said slurry composition further comprising: between about 0.1gm/liter and about 5 gm/liter a copper corrosion inhibitor.
 12. Themethod of claim 5, wherein said octanol is 1-octanol.
 13. A method,comprising: providing an aqueous slurry composition on a surface to bepolished, said slurry composition comprising: abrasive particles; ferricnitrate; a surfactant anion; octanol; and water as a diluent; andpolishing said surface by contacting said surface with a polishing pad.14. the method of claim 13, said slurry composition further comprising acopper corrosion inhibitor.
 15. The method of claim 13, said slurrycomposition further comprising: a chloride ion source; and a sulfate ionsource.
 16. The method of claim 1, wherein the surface tension of saidslurry composition is between 30 dynes/cm² and 27 dynes/cm².
 17. Themethod of claim 5, wherein the surface tension of said slurrycomposition is between 30 dynes/cm² and 27 dynes/cm².
 18. The method ofclaim 13, wherein the surface tension of said slurry composition isbetween 30 dynes/cm² and 27 dynes/cm².